中温回火（250－500度）中温回火所得组织为回火屈氏体。其目的是获得高的屈服强度，弹性极限和较高的韧性。

Medium temperature tempering (250-500 degrees)，无锡搪瓷管， medium temperature tempering income group as tempered troostite. Its is to obtain high yield strength， elastic limit and high toughness.

因此，它主要用于各种GB/T9711.1搪瓷管和热作模具的处理，回火后硬度一般为HRC35－50。

Therefore， it is mainly used for various kinds of GB/T9711.1 enamel tube and hot mould processing， after tempering hardness is HRC35-50 commonly.

低温回火（150－250度）低温回火所得组织为回火马氏体。其目的是在保持淬火钢的高硬度和高耐磨性的前提下，降低其淬火内应力和脆性，以免使用时崩裂或过早损坏。

Low temperature tempering (150-250 degrees)， low temperature tempering the organization for the tempered martensite. Its aim is to keep a hardened steel under the premise of high hardness and high wear resistance， decrease the quenching stress and brittleness，搪瓷管加工， lest when using split or premature failure.

它主要用于各种高碳的切削刃具，量具，GB/T9711.1搪瓷管，滚动轴承以及渗碳件等，回火后硬度一般为HRC58－64。

It is mainly used for cutting all kinds of high carbon cutting， measuring tool， GB/T9711.1 enamel tube， such as pieces of rolling bearing and carburizing， after tempering hardness is commonly HRC58-64.

本文由搪瓷管热能科技有限公司友情奉献.更多有关的知识请点击:http://www.jrrnkj.com/我们将用先进的技术.真诚的态度.为您提供优质的服务.更多有关的知识我们将会陆续向大家奉献.敬请期待.

搪瓷管能有效防止腐蚀

      石化企业在生产过程中几乎无处不存在着各种类型和不同腐蚀程度的腐蚀问题。目前，这种状况随着加工含硫量的增加而日趋严重，2017年搪瓷管，并影响正常的生产，甚至危及设备的安全，因设备腐蚀泄漏而造成非正常停车等事故时有发生。

　　因此采用可靠经济的方法提高设备耐腐蚀能力是石化企业和设备制造厂都迫切需要解决的课题。搪瓷管换热器，正是结合目前石化生产装置的工艺要求和高硫加工量逐渐增大、炼油装置设备腐蚀加剧的具体情况，而开发的经济可靠且用途广泛的防腐蚀设备碳素钢冷换设备的腐蚀特性用于石油化工行业的碳素钢换热器所发生的金属腐蚀性基本是电化学腐蚀和化学腐蚀，这是由于中的无机盐、硫化物、氮化合物和水等腐蚀介质在加工过程中不同温度下存在不同腐蚀的作用，各种的腐蚀介质有其各异的腐蚀特性。